Search for: All records

A novel processing method that creates and preserves ceramic nanoparticles in solid oxide electrodes during co-sintering at traditional sintering temperatures is introduced. Specifically, carbon templated samarium-doped ceria nanoparticles (nSDC) were successfully integrated with commercial lanthanum strontium cobalt ferrite (LSCF) and commercial SDC powders, producing LSCF-SDC-nSDC cathodes upon processing. The effect of nSDC concentration on cathode electrocatalytic activity was investigated at low operational temperatures, 600 °C–700 °C, with symmetrical cells. Low nSDC loadings, ≤5 wt% nSDC, significantly decreased cell polarization resistance whereas higher loadings increased it. The best electrochemical performance was achieved with 5 wt% nSDC, lowering the polarization resistance by 41% at 600 °C. Fuel cell tests demonstrate that adding 5 wt% nSDC increased the maximum fuel cell power density by 38%. Electrochemical impedance spectra showed substantial improvements in both fuel cell polarization resistance and ohmic resistance, indicating that nSDC increased the electrocatalytically active area of the cathode. This work demonstrates a simple, novel method for effectively increasing electrocatalytic activity of solid oxide electrodes at low operational temperatures. 

The impact of infiltrating chloride salts on the electrochemical behavior of lanthanum strontium manganite-yttria stabilized zirconia (LSM-YSZ) cathodes was investigated under solid oxide fuel cell operation. Infiltrating a lanthanum chloride solution resulted in the formation of a lanthanum oxychloride (LaOCl) phase. A LaOCl phase also formed by infiltrating an ammonium chloride solution; however, lanthanum was scavenged from the LSM phase to form LaOCl. The third infiltrating solution, a combination of zirconium chloride and yttrium nitrate, formed LaOCl by scavenging lanthanum from LSM and produced YSZ nanoparticles. Electrochemical impedance spectroscopy results suggest that LaOCl improves oxygen adsorption kinetics compared to a baseline LSM-YSZ cathode, reducing the low frequency impedance by 30%. In addition, scavenging lanthanum from LSM improved oxygen ion diffusion polarization as indicated by the observed 40% reduction in high frequency impedance and improved serial ohmic resistance by 19%. Finally, YSZ nanoparticles further reduced the high frequency impedance and ohmic resistance by 45% and 23%, respectively. The findings reveal new strategies for lowering the impedance of LSM-YSZ cathodes. 

The thermochemical stability of lanthanum strontium cobalt ferrite (LSCF) processed between 1000 °C–1200 °C via the in situ carbon templating method was studied. This method generates high surface area ceramics at traditional solid oxide fuel cell (SOFC) sintering temperatures by generating a carbon template in situ and subsequently removing the template by oxidation at 700 °C. Argon processed samples produced an amorphous carbon template, whereas nitrogen tended to form graphitic carbon. Prior to the oxidation step, nitrogen samples comprised larger La 2 O 3 crystallites (22–40 nm) compared to argon (9–17 nm). Upon oxidation, argon samples resulted in a pure LSCF phase with surface areas in the 21–29 m 2 ·g −1 range, whereas nitrogen samples contained significant impurities. This demonstrates that the size of La 2 O 3 crystallites formed during inert processing limited the ability to produce a pure LSCF phase. Symmetrical cells comprising nano-LSCF electrodes generated by the templating method were compared to cells sintered directly in air. Impedance results suggest that nano-LSCF cells and cells processed in air were dominated by interfacial charge transfer resistance and gas diffusion, respectively. The results map out conditions for preparing and integrating high surface area, nanostructured LSCF into SOFC electrodes at traditional sintering temperatures. Strategies for improving the interfacial resistance of nano-LSCF electrodes are discussed.